ansys的粘弹性输入，似乎一直是一个大家都不愿意多谈的问题。小弟从事一项沥青路面的仿真项目，没有办法，最后自己摸索了一下子。一下是自己的一点经验：
粘弹性模型，一般为广义maxwell和burgers及广义burgers模型居多，置于简单的maxwell和kelvin模型，这里不多谈了。广义maxwell模型的输入，一般需要输入的是c46，c50，c51－c60，c61－c70 。其中c46是n个maxwell模型的剪切模量的和，E一般是拉伸模量，要转化为剪切模量，至于转化的方法，详见粘弹性理论专业书籍！ c50是maxwell单元个数n，ansys最多支持10个maxwell单元并列。c51－c60是单个maxwell单元的剪切模量Ei/c46，c61－70是maxwell单元的ni/Ei，注意c61－c70的和为1。至于体积松弛模量一般用不到，这里也就不谈了。另外一个重要的是时温方程的输入，如果用的是WLF方程，需要输入的是c5＝1，c1，c2是WLF的两个方程常数，c4一般为玻璃化温度。如果是TN方程，c5＝0，c1＝H/R.其中H是表面活化能，R是气体普适常数。c2就是TN方程中的x。用TN方程的时候要注意，方程中的Tref要用命令TREF输入，不能够从窗口直接输入。另外大家经常碰到的文献中说的Arrhenius公式，其实就是TN方程当x＝0的一个特例。
以下是我输入的一段关于沥青混合料的log语言：
/prep7
et,1,185
tref,268
TB,EVIS,1,,,0
TBMODIF,1,1,20110
TBMODIF,1,2,0
TBMODIF,1,3,
TBMODIF,1,4,
TBMODIF,1,5,0
TBMODIF,2,1,
TBMODIF,2,2,
TBMODIF,2,3,
TBMODIF,2,4,
TBMODIF,2,5,
TBMODIF,3,1,
TBMODIF,3,2,
TBMODIF,3,3,
TBMODIF,3,4,
TBMODIF,3,5,
TBMODIF,4,1,
TBMODIF,4,2,
TBMODIF,4,3,
TBMODIF,4,4,
TBMODIF,4,5,
TBMODIF,5,1,
TBMODIF,5,2,
TBMODIF,5,3,
TBMODIF,5,4,
TBMODIF,5,5,
TBMODIF,6,1,
TBMODIF,6,2,
TBMODIF,6,3,
TBMODIF,6,4,
TBMODIF,6,5,
TBMODIF,7,1,
TBMODIF,7,2,
TBMODIF,7,3,
TBMODIF,7,4,
TBMODIF,7,5,
TBMODIF,8,1,
TBMODIF,8,2,
TBMODIF,8,3,
TBMODIF,8,4,
TBMODIF,8,5,
TBMODIF,9,1,
TBMODIF,9,2,
TBMODIF,9,3,
TBMODIF,9,4,
TBMODIF,9,5,
TBMODIF,10,1,1.9798e10
TBMODIF,10,2,
TBMODIF,10,3,
TBMODIF,10,4,
TBMODIF,10,5,6
TBMODIF,11,1,0.033332
TBMODIF,11,2,0.525813
TBMODIF,11,3,0.128042
TBMODIF,11,4,0.02184
TBMODIF,11,5,0.20952
TBMODIF,12,1,0.081473
TBMODIF,12,2,
TBMODIF,12,3,
TBMODIF,12,4,
TBMODIF,12,5,
TBMODIF,13,1,1.315e6
TBMODIF,13,2,32.13
TBMODIF,13,3,986.4
TBMODIF,13,4,1.451e5
TBMODIF,13,5,191.6
TBMODIF,14,1,7570
TBMODIF,14,2,
TBMODIF,14,3,
TBMODIF,14,4,
TBMODIF,14,5,
TBMODIF,15,1,
TBMODIF,15,2,
TBMODIF,15,3,
TBMODIF,15,4,
TBMODIF,15,5,
TBMODIF,16,1,
TBMODIF,16,2,
TBMODIF,16,3,
TBMODIF,16,4,
TBMODIF,16,5,
TBMODIF,17,1,
TBMODIF,17,2,
TBMODIF,17,3,
TBMODIF,17,4,
TBMODIF,17,5,
TBMODIF,18,1,
TBMODIF,18,2,
TBMODIF,18,3,
TBMODIF,18,4,
TBMODIF,18,5,
TBMODIF,19,1,
TBMODIF,19,2,
TBMODIF,19,3,
TBMODIF,19,4,
TBMODIF,19,5,